Macrocellular and microcellular SiOC open cell ceramic foams were fabricated from a preceramic polymer. Macrocellular foams, with a cell size ranging from about 100-600 mum and a bulk density ranging from about 0.25-0.58 g/cm(3), depending on the processing parameters, were fabricated using a direct foaming approach. Microcellular foams, with a cell size of about 8 mum, were fabricated using poly(methyl methacrylate)microbeads as sacrificial templates. The bulk density ranged from about 0.31-0.48 g/cm 3, depending on the amount of microbeads in the starting material. The compression strength of the foams increased with increasing relative density, and microcellular foams possessed a 2-5 times higher crushing strength than macrocellular foams of similar density.
Macro- and micro-cellular porous ceramics from preceramic polymers
COLOMBO, PAOLO;BERNARDO, ENRICO
2003
Abstract
Macrocellular and microcellular SiOC open cell ceramic foams were fabricated from a preceramic polymer. Macrocellular foams, with a cell size ranging from about 100-600 mum and a bulk density ranging from about 0.25-0.58 g/cm(3), depending on the processing parameters, were fabricated using a direct foaming approach. Microcellular foams, with a cell size of about 8 mum, were fabricated using poly(methyl methacrylate)microbeads as sacrificial templates. The bulk density ranged from about 0.31-0.48 g/cm 3, depending on the amount of microbeads in the starting material. The compression strength of the foams increased with increasing relative density, and microcellular foams possessed a 2-5 times higher crushing strength than macrocellular foams of similar density.Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.