The paper presents an experimental investigation based on hydrostatic micro extrusion of billets in low carbon steel and commercially pure copper, and the relevant results. The starting billets have a diameter of 0.3 mm and are 5 mm long; a high pressure generator consisting of a manually operated piston screw pump is used to pressurize the fluid up to 4200 bar, the screw pump is connected through a 3-way distribution block to the extrusion die and to a strain gauge high pressure sensor. The sensor has a full scale of 5000 bar and the extrusion pressure is acquired at a sampling rate of 2 kHz by means of an acquisition program written in the LabVIEW environment. Tests have been conducted at room temperature and a lubricant for wire drawing (Chemetall Gardolube DO 338) acts both as the pressurizing fluid and lubricant too. In addition, billets were graphite coated. Different fluid pressures and process durations have been adopted, resulting in different extrusion lengths. The required extrusion pressure is much higher than in non-micro forming operations (this effect is more evident for steel). On the cross section of the extruded parts, hardness and grain size distribution have been measured, the former through Vickers micro hardness (10 g load) tests. In the case of the extrusion of copper, the material behaves as in microdrawing process. In the case of the extrusion of steel, the hardness increases from the core to the surface as in the drawing process, but with lower values. The analysis evidenced the presence of the external layer, but its thickness is about 1/3 of the external layer in the drawn wire and the grains appear smaller than in the layer of the drawn wire. The extruding force required along the extruding direction is higher (22 - 24 N) than the drawing force along the same direction (12 N): being the material, the reduction ratio, the die sliding length the same in both cases, the higher extrusion force should be caused by a higher tangential friction force and/or a higher redundant work of deformation and/or a different material behaviour. Which is the real mechanism is not clear at present, but surface layer grains in extrusion are more deformed than in wire drawing. For this reason the deformation inhomogeneity increases in extrusion and the material under the highly deformed surface layer should be subjected to lower strains, strain hardening and finally resulting in lower hardness.

Hydrostatic microextrusion of steel and copper

BERTI, GUIDO;MONTI, MANUEL;
2011

Abstract

The paper presents an experimental investigation based on hydrostatic micro extrusion of billets in low carbon steel and commercially pure copper, and the relevant results. The starting billets have a diameter of 0.3 mm and are 5 mm long; a high pressure generator consisting of a manually operated piston screw pump is used to pressurize the fluid up to 4200 bar, the screw pump is connected through a 3-way distribution block to the extrusion die and to a strain gauge high pressure sensor. The sensor has a full scale of 5000 bar and the extrusion pressure is acquired at a sampling rate of 2 kHz by means of an acquisition program written in the LabVIEW environment. Tests have been conducted at room temperature and a lubricant for wire drawing (Chemetall Gardolube DO 338) acts both as the pressurizing fluid and lubricant too. In addition, billets were graphite coated. Different fluid pressures and process durations have been adopted, resulting in different extrusion lengths. The required extrusion pressure is much higher than in non-micro forming operations (this effect is more evident for steel). On the cross section of the extruded parts, hardness and grain size distribution have been measured, the former through Vickers micro hardness (10 g load) tests. In the case of the extrusion of copper, the material behaves as in microdrawing process. In the case of the extrusion of steel, the hardness increases from the core to the surface as in the drawing process, but with lower values. The analysis evidenced the presence of the external layer, but its thickness is about 1/3 of the external layer in the drawn wire and the grains appear smaller than in the layer of the drawn wire. The extruding force required along the extruding direction is higher (22 - 24 N) than the drawing force along the same direction (12 N): being the material, the reduction ratio, the die sliding length the same in both cases, the higher extrusion force should be caused by a higher tangential friction force and/or a higher redundant work of deformation and/or a different material behaviour. Which is the real mechanism is not clear at present, but surface layer grains in extrusion are more deformed than in wire drawing. For this reason the deformation inhomogeneity increases in extrusion and the material under the highly deformed surface layer should be subjected to lower strains, strain hardening and finally resulting in lower hardness.
2011
AIP Conference Proceedings, Volume 1353The 14th International ESAFORM Conference on Material FormingEsaform 2011
9780735409118
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11577/2480103
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 2
  • ???jsp.display-item.citation.isi??? 2
social impact