The precipitation of primary Fe-bearing compounds in a secondary AlSi9Cu3(Fe) alloy has been investigated over three levels of iron (0.80, 1.00, 1.20 mass%) and manganese (0.25, 0.40, 0.55 mass%), and two levels of chromium (0.06, 0.10 mass%), as well as different cooling rates (2, 10, 20 °C min-1). Differential scanning calorimetry and metallographic techniques have been used in order to quantitatively evaluate the nucleation temperature and the phase fraction of sludge particles. The temperature of sludge formation increases by increasing the initial concentrations of Fe, Mn and Cr, while an increase in the cooling rate shifts the sludge nucleation towards lower temperature. The amount of sludge particles increases progressively with the sludge factor but even more by decreasing the cooling rate. The combination of Fe, Mn and Cr levels, as well as cooling rate, allows to determine a threshold value that prevents the sludge formation. In the analysed range of composition and cooling conditions, functional equations have been developed in order to accurately predict the precipitation temperature and the phase fraction of sludge in AlSi9Cu3(Fe) die-casting alloys.

Precipitation of primary Fe-rich compounds in secondary AlSi9Cu3(Fe) alloys

TIMELLI, GIULIO;CAPUZZI, STEFANO;FABRIZI, ALBERTO
2016

Abstract

The precipitation of primary Fe-bearing compounds in a secondary AlSi9Cu3(Fe) alloy has been investigated over three levels of iron (0.80, 1.00, 1.20 mass%) and manganese (0.25, 0.40, 0.55 mass%), and two levels of chromium (0.06, 0.10 mass%), as well as different cooling rates (2, 10, 20 °C min-1). Differential scanning calorimetry and metallographic techniques have been used in order to quantitatively evaluate the nucleation temperature and the phase fraction of sludge particles. The temperature of sludge formation increases by increasing the initial concentrations of Fe, Mn and Cr, while an increase in the cooling rate shifts the sludge nucleation towards lower temperature. The amount of sludge particles increases progressively with the sludge factor but even more by decreasing the cooling rate. The combination of Fe, Mn and Cr levels, as well as cooling rate, allows to determine a threshold value that prevents the sludge formation. In the analysed range of composition and cooling conditions, functional equations have been developed in order to accurately predict the precipitation temperature and the phase fraction of sludge in AlSi9Cu3(Fe) die-casting alloys.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11577/3185181
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 37
  • ???jsp.display-item.citation.isi??? 37
social impact