Effect of in-mould inoculant composition on microstructure and fatigue behaviour of heavy section ductile iron castings

In this paper, the influence of the in-mould inoculant composition on microstructure and fatigue behaviour of heavy section ductile iron (EN GJS 700-2) castings has been investigated. Axial fatigue tests under nominal load ratio R=0 have been performed on specimens taken from the core of large casting components. Metallographic analyses have been carried out by means of optical microscopy and important microstructural parameters that affect the mechanical properties of the alloy, such as nodule count, nodularity and graphite shape, were measured. Furthermore, Scanning Electron Microscopy was used to investigate the fracture surfaces of the samples in order to identify crack initiation and propagation zones. Cracks initiation sites have been found to be microshrinkages close to specimens’ surface in most cases. It was found that in-mould inoculant composition strongly influences the alloy microstructure, such as nodule count and shrinkage porosities size, as well as the fatigue resistance of heavy section ductile iron castings.