Abstract The interface structure of epitaxial Fe/Cr multilayers was studied using anomalous X-ray and neutron reflectivity. The analysis of X-ray reflectivity at three different energies provided a reliable information about the interface roughnesses. It is found that the Cr-on-Fe interface is more diffused as compared to the Fe-on-Cr interface and that the roughness exhibits a significant increase with increasing depth. The magnetic roughness, as determined from neutron reflectivity, is lower than the geometrical roughness, in conformity with the behavior of a number of magnetic thin films and multilayers.
Structural characterization of epitaxial Fe/Cr multilayers using anomalous X-ray and neutron reflectivity
MADDALENA, AMEDEO;PRINCIPI, GIOVANNI
2004
Abstract
Abstract The interface structure of epitaxial Fe/Cr multilayers was studied using anomalous X-ray and neutron reflectivity. The analysis of X-ray reflectivity at three different energies provided a reliable information about the interface roughnesses. It is found that the Cr-on-Fe interface is more diffused as compared to the Fe-on-Cr interface and that the roughness exhibits a significant increase with increasing depth. The magnetic roughness, as determined from neutron reflectivity, is lower than the geometrical roughness, in conformity with the behavior of a number of magnetic thin films and multilayers.File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.