The morphology, structure and melting behaviour of cold-crystallized isotactic polystyrene (iPS) were studied by differential scanning calorimetry (DSC), wide angle X-ray diffraction (WAXD) and small angle X-ray scattering (SAXS). The polymer was found to crystallize according to the dual-lamellar stack model. The two populations of lamellae, along with a melting-recrystallization phenomenon, determined the appearance of multiple melting peaks in DSC traces. The annealing peak was attributed to the relaxation. of a rigid amorphous phase, rather than to the melting of crystalline material
The morphology, structure and melting behaviour of cold crystallized isotactic polystyrene
MAREGA, CARLA;CAUSIN, VALERIO;MARIGO, ANTONIO
2006
Abstract
The morphology, structure and melting behaviour of cold-crystallized isotactic polystyrene (iPS) were studied by differential scanning calorimetry (DSC), wide angle X-ray diffraction (WAXD) and small angle X-ray scattering (SAXS). The polymer was found to crystallize according to the dual-lamellar stack model. The two populations of lamellae, along with a melting-recrystallization phenomenon, determined the appearance of multiple melting peaks in DSC traces. The annealing peak was attributed to the relaxation. of a rigid amorphous phase, rather than to the melting of crystalline materialFile in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.