Sol– gel derived silica (SiO2) films doped with nickel oxide (NiO) nanocrystals were fabricated. A bifunctional ligand was used, bearing amine groups capable of coordinating the nickel ions and hydrolysable siloxane groups for anchoring the metal complex moiety to the silicate matrix. Nickel oxide nanocrystals precipitated at 500°C while the film was still porous. The nanocomposite films showed a reversible change in the optical transmittance in the VIS-NIR range when exposed to carbon monoxide gas. The effects of residual porosity, testing temperature, and carbon monoxide gas concentration on optical transmittance were studied.

Nanostructured SiO2-NiO sol-gel films with enhanced optical CO gas sensitivity

MARTUCCI, ALESSANDRO;GUGLIELMI, MASSIMO;
2003

Abstract

Sol– gel derived silica (SiO2) films doped with nickel oxide (NiO) nanocrystals were fabricated. A bifunctional ligand was used, bearing amine groups capable of coordinating the nickel ions and hydrolysable siloxane groups for anchoring the metal complex moiety to the silicate matrix. Nickel oxide nanocrystals precipitated at 500°C while the film was still porous. The nanocomposite films showed a reversible change in the optical transmittance in the VIS-NIR range when exposed to carbon monoxide gas. The effects of residual porosity, testing temperature, and carbon monoxide gas concentration on optical transmittance were studied.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11577/2460139
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 38
  • ???jsp.display-item.citation.isi??? 33
social impact