Padua Research Archive, l’archivio istituzionale della produzione scientifica dell’Università degli Studi di Padova, ha lo scopo di raccogliere, documentare, conservare e pubblicare, anche ad accesso aperto, i prodotti della ricerca dell’Ateneo. Padua Research Archive utilizza la piattaforma IRIS (Institutional Research Information System) sviluppata da Cineca.
EnglishMacrocellular and microcellular SiOC open cell ceramic foams were fabricated from a preceramic polymer. Macrocellular foams, with a cell size ranging from about 100-600 mum and a bulk density ranging from about 0.25-0.58 g/cm(3), depending on the processing parameters, were fabricated using a direct foaming approach. Microcellular foams, with a cell size of about 8 mum, were fabricated using poly(methyl methacrylate)microbeads as sacrificial templates. The bulk density ranged from about 0.31-0.48 g/cm 3, depending on the amount of microbeads in the starting material. The compression strength of the foams increased with increasing relative density, and microcellular foams possessed a 2-5 times higher crushing strength than macrocellular foams of similar density.
| Titolo: | Macro- and micro-cellular porous ceramics from preceramic polymers |
| Autori: | |
| Data di pubblicazione: | 2003 |
| Rivista: | |
| Abstract: | Macrocellular and microcellular SiOC open cell ceramic foams were fabricated from a preceramic polymer. Macrocellular foams, with a cell size ranging from about 100-600 mum and a bulk density ranging from about 0.25-0.58 g/cm(3), depending on the processing parameters, were fabricated using a direct foaming approach. Microcellular foams, with a cell size of about 8 mum, were fabricated using poly(methyl methacrylate)microbeads as sacrificial templates. The bulk density ranged from about 0.31-0.48 g/cm 3, depending on the amount of microbeads in the starting material. The compression strength of the foams increased with increasing relative density, and microcellular foams possessed a 2-5 times higher crushing strength than macrocellular foams of similar density. |
| Handle: | http://hdl.handle.net/11577/2461821 |
| Appare nelle tipologie: | 01.01 - Articolo in rivista |
File in questo prodotto:
http://hdl.handle.net/11577/2461821
Copyright © 2019