The synthesis and characterization of low k one-dimensional (1D) hybrid organic organometallic supramolecular ribbons 3a,b, through halogen-bond driven co-crystallization of trans-[Pt(PCy3)2(C C-4-py)2] (1) with 1,4-diiodotetrafluorobenzene (2a) and trans-1,2-bis-(2,3,5,6-tetrafluoro-44odopheny1)-ethylene (2b), are reported. The co-crystals 3a,b have been obtained by isothermal evaporation of a chloroform solution containing the corresponding starting materials at room temperature. X-ray structure determinations show that noncovalent interactions other than halogen bonds help in the construction of the crystal packing; these interactions are stronger in 3b, thus reducing the chain mobility with respect to 3a. Accordingly, the broadband dielectric spectroscopic determinations, carried out from 10-2 Hz to 10 MHz and at a temperature ranging from 25 to 155 °C, showed that both 3a and 3b materials exhibit a real component of dielectric permittivity significantly lower than SiO2. In particular in the case of 3b, the rigidity of the ID chain explains the observed epsilon and tan delta values. A permittivity value that is significantly lower than that of the silica reference, tan delta values lower than 0.02 in the entire investigated temperature range, and less than 0.004 at T < 100 °C make 3b a very promising low k hybrid organic organometallic material for application as dielectric films in next generation microelectronics.

Interplay between Structural and Dielectric Features of New Low k Hybrid Organic-Organometallic Supramolecular Ribbons

SGARBOSSA, PAOLO;BERTANI, ROBERTA;DI NOTO, VITO;PIGA, MATTEO;GIFFIN, GUINEVERE;
2012

Abstract

The synthesis and characterization of low k one-dimensional (1D) hybrid organic organometallic supramolecular ribbons 3a,b, through halogen-bond driven co-crystallization of trans-[Pt(PCy3)2(C C-4-py)2] (1) with 1,4-diiodotetrafluorobenzene (2a) and trans-1,2-bis-(2,3,5,6-tetrafluoro-44odopheny1)-ethylene (2b), are reported. The co-crystals 3a,b have been obtained by isothermal evaporation of a chloroform solution containing the corresponding starting materials at room temperature. X-ray structure determinations show that noncovalent interactions other than halogen bonds help in the construction of the crystal packing; these interactions are stronger in 3b, thus reducing the chain mobility with respect to 3a. Accordingly, the broadband dielectric spectroscopic determinations, carried out from 10-2 Hz to 10 MHz and at a temperature ranging from 25 to 155 °C, showed that both 3a and 3b materials exhibit a real component of dielectric permittivity significantly lower than SiO2. In particular in the case of 3b, the rigidity of the ID chain explains the observed epsilon and tan delta values. A permittivity value that is significantly lower than that of the silica reference, tan delta values lower than 0.02 in the entire investigated temperature range, and less than 0.004 at T < 100 °C make 3b a very promising low k hybrid organic organometallic material for application as dielectric films in next generation microelectronics.
2012
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11577/2483624
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 48
  • ???jsp.display-item.citation.isi??? 48
  • OpenAlex ND
social impact