A stable Eu3+→Eu2+ reduction is accomplished by thermal annealing in N2 ambient of Eu2O3 films deposited by magnetron sputtering on Si substrates. Transmission electron microscopy and x-ray diffraction measurements demonstrate the occurrence of a complex reactivity at the Eu2O3/Si interface, leading to the formation of Eu2+ silicates, characterized by a very strong (the measured external quantum efficiency is about 10%) and broad room temperature photoluminescence (PL) peak centered at 590 nm. This signal is much more efficient than the Eu3+ emission, mainly consisting of a sharp PL peak at 622 nm, observed in O2-annealed films, where the presence of a SiO2 layer at the Eu2O3/Si interface prevents Eu2+ formation.

Eu^3+ reduction and efficient light emission in Eu_2O_3 films deposited on Si substrates

CESCA, TIZIANA;
2012

Abstract

A stable Eu3+→Eu2+ reduction is accomplished by thermal annealing in N2 ambient of Eu2O3 films deposited by magnetron sputtering on Si substrates. Transmission electron microscopy and x-ray diffraction measurements demonstrate the occurrence of a complex reactivity at the Eu2O3/Si interface, leading to the formation of Eu2+ silicates, characterized by a very strong (the measured external quantum efficiency is about 10%) and broad room temperature photoluminescence (PL) peak centered at 590 nm. This signal is much more efficient than the Eu3+ emission, mainly consisting of a sharp PL peak at 622 nm, observed in O2-annealed films, where the presence of a SiO2 layer at the Eu2O3/Si interface prevents Eu2+ formation.
2012
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11577/2490087
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 28
  • ???jsp.display-item.citation.isi??? 26
social impact