Self foaming cellular glass-ceramics were obtained by sintering mixtures of a basalt scoria and soda lime cullet for 15 min at 1050 and 1100 °C. The effect of polyvalent ions (Fe3 +/Fe2 +) on porosity (from 53 to 86 vol.%) and crystallization was studied for different mixtures subjected to different thermal treatments. Due to the range of mechanical strength values (crushing strength from 2 to 50 MPa) and total porosity achieved, these porous glass-ceramics could be applied as building materials, as lightweight aggregate for concrete or as lightweight panels.

Cellular glass–ceramics from a self foaming mixture of glass and basalt scoria

MARANGONI, MAURO;SECCO, MICHELE;PARISATTO, MATTEO;ARTIOLI, GILBERTO;BERNARDO, ENRICO;COLOMBO, PAOLO;
2014

Abstract

Self foaming cellular glass-ceramics were obtained by sintering mixtures of a basalt scoria and soda lime cullet for 15 min at 1050 and 1100 °C. The effect of polyvalent ions (Fe3 +/Fe2 +) on porosity (from 53 to 86 vol.%) and crystallization was studied for different mixtures subjected to different thermal treatments. Due to the range of mechanical strength values (crushing strength from 2 to 50 MPa) and total porosity achieved, these porous glass-ceramics could be applied as building materials, as lightweight aggregate for concrete or as lightweight panels.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Caricamento pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11577/3035322
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 36
  • ???jsp.display-item.citation.isi??? 33
social impact