MOS capacitors with a 4.4 nm thick gate oxide have been exposed to gamma radiation from a Co-60 source. As a result, we have measured a stable leakage current at fields lower than those required for Fowler-Nordheim tunneling. This Radiation Induced Leakage Current (RILC) is similar to the usual Stress Induced Leakage Currents (SILC) observed after electrical stresses of MOS devices. We have verified that these two currents share the same dependence on the oxide field, and the RILC contribution can be normalized to an equivalent injected charge for Constant Current Stresses. We have also considered the dependence of the RILC from the cumulative radiation dose, and from the applied bias during irradiation, suggesting a correlation between RILC and the distribution of trapped holes and neutral levels in the oxide layer.
Ionizing radiation induced leakage current on ultra-thin gate oxides
PACCAGNELLA, ALESSANDRO;
1997
Abstract
MOS capacitors with a 4.4 nm thick gate oxide have been exposed to gamma radiation from a Co-60 source. As a result, we have measured a stable leakage current at fields lower than those required for Fowler-Nordheim tunneling. This Radiation Induced Leakage Current (RILC) is similar to the usual Stress Induced Leakage Currents (SILC) observed after electrical stresses of MOS devices. We have verified that these two currents share the same dependence on the oxide field, and the RILC contribution can be normalized to an equivalent injected charge for Constant Current Stresses. We have also considered the dependence of the RILC from the cumulative radiation dose, and from the applied bias during irradiation, suggesting a correlation between RILC and the distribution of trapped holes and neutral levels in the oxide layer.Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.