In the present, the high cycle fatigue strength of notched ductile cast iron is investigated. Experimental tests under axial loading, has been carried out on sharp V-notched specimens taken from heavy section casting considering nominal load ratios (R = 0). All specimens, taken from a heavy section casting, are characterized by a notch tip radius less than 0.1. mm, a notch depth of 10. mm and a notch opening angle = 90°. In order to evaluate the influence of chunky graphite morphology on fatigue life, fatigue tests were carried out also on a second set of specimens without that microstructural defect.Metallurgical analyses were performed on all the samples and some important microstructural parameters (nodule count and nodularity rating, among others) were measured and compared. It was found that a mean content of 40% of chunky graphite in the microstructure (with respect to total graphite content) does not influence significantly the fatigue strength properties of the analysed cast iron.
Fatigue strength of sharp V-notched specimens made of ductile cast iron
BERTO, FILIPPO;FERRO, PAOLO;
2017
Abstract
In the present, the high cycle fatigue strength of notched ductile cast iron is investigated. Experimental tests under axial loading, has been carried out on sharp V-notched specimens taken from heavy section casting considering nominal load ratios (R = 0). All specimens, taken from a heavy section casting, are characterized by a notch tip radius less than 0.1. mm, a notch depth of 10. mm and a notch opening angle = 90°. In order to evaluate the influence of chunky graphite morphology on fatigue life, fatigue tests were carried out also on a second set of specimens without that microstructural defect.Metallurgical analyses were performed on all the samples and some important microstructural parameters (nodule count and nodularity rating, among others) were measured and compared. It was found that a mean content of 40% of chunky graphite in the microstructure (with respect to total graphite content) does not influence significantly the fatigue strength properties of the analysed cast iron.Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.