The development of molecularly homogeneous multicomponent oxide based glasses is a key concern in many fields of materials chemistry. Oxide nanoparticles covalently embedded in dielectric matrices represent a class of nanocomposite systems endowed with outstanding optical, mechanical, electronic, and thermal properties. In this study, silica thin films embedding HfO2 were prepared by dip-coating on silica glass via a modified sol-gel processing. This powerful synthetic method, mainly based on the hydrolysis and condensation of metal alkoxides, provides a reliable route to oxide materials which can be processed into a variety of different forms (thin films, powders, monoliths, etc.). The novel synthetic route here presented is based on the copolymerization of the organically modified oxohafnium clusters (Hf4O2(OMc)12 with OMc = OC(O)–C(CH3)=CH2)) with (methacryloxymethyl)triethoxysilane (MAMTES). The crystalline clusters, which are the precursors for the corresponding metal oxide (MO2) were prepared via the sol-gel route by reaction of hafnium butoxide with methacrylic acid. The copolymerization of the cluster with previously prehydrolysed methacrylate-functionalized siloxane, allows the anchoring of the oxocluster to the forming silica network. Thin films were prepared starting from a THF (tetrahydrofurane) solution with molar ratios Hf4O2(OMc)12:MAMTES of 1:44 and a MAMTES:THF molar ratio of 1:5, which was stirred at room temperature for 8 h. After deposition, the film was annealed 3 h at 800 °C in air to promote the decomposition of the hafnium oxocluster to give the corresponding HfO2. The obtained HfO2-SiO2 film resulted transparent and homogeneous. The composition of the film was investigated by secondary ionization mass spectrometry (SIMS) and x-ray photoelectron spectroscopy (XPS), which were used also to investigate the in-depth distribution. The depth profiles evidenced a very homogenous distribution of hafnium within the whole silica film and a sharp film-substrate interface. TEM micrographs revealed the formation of isolated nanocrystalline particles, thus ruling out the formation of a HfO2–SiO2 mixture. Concerning the herewith reported XPS analyses, the main XPS core-levels were analyzed for the sample annealed 3 h at 800 °C. The formation of hafnium oxide was evidenced. Furthermore, a very homogeneous distribution of the guest oxide in the host matrix was evidenced, in agreement with SIMS data.

HfO2-doped Silica Thin Films by XPS

Armelao L
;
GROSS, SILVIA;
2005

Abstract

The development of molecularly homogeneous multicomponent oxide based glasses is a key concern in many fields of materials chemistry. Oxide nanoparticles covalently embedded in dielectric matrices represent a class of nanocomposite systems endowed with outstanding optical, mechanical, electronic, and thermal properties. In this study, silica thin films embedding HfO2 were prepared by dip-coating on silica glass via a modified sol-gel processing. This powerful synthetic method, mainly based on the hydrolysis and condensation of metal alkoxides, provides a reliable route to oxide materials which can be processed into a variety of different forms (thin films, powders, monoliths, etc.). The novel synthetic route here presented is based on the copolymerization of the organically modified oxohafnium clusters (Hf4O2(OMc)12 with OMc = OC(O)–C(CH3)=CH2)) with (methacryloxymethyl)triethoxysilane (MAMTES). The crystalline clusters, which are the precursors for the corresponding metal oxide (MO2) were prepared via the sol-gel route by reaction of hafnium butoxide with methacrylic acid. The copolymerization of the cluster with previously prehydrolysed methacrylate-functionalized siloxane, allows the anchoring of the oxocluster to the forming silica network. Thin films were prepared starting from a THF (tetrahydrofurane) solution with molar ratios Hf4O2(OMc)12:MAMTES of 1:44 and a MAMTES:THF molar ratio of 1:5, which was stirred at room temperature for 8 h. After deposition, the film was annealed 3 h at 800 °C in air to promote the decomposition of the hafnium oxocluster to give the corresponding HfO2. The obtained HfO2-SiO2 film resulted transparent and homogeneous. The composition of the film was investigated by secondary ionization mass spectrometry (SIMS) and x-ray photoelectron spectroscopy (XPS), which were used also to investigate the in-depth distribution. The depth profiles evidenced a very homogenous distribution of hafnium within the whole silica film and a sharp film-substrate interface. TEM micrographs revealed the formation of isolated nanocrystalline particles, thus ruling out the formation of a HfO2–SiO2 mixture. Concerning the herewith reported XPS analyses, the main XPS core-levels were analyzed for the sample annealed 3 h at 800 °C. The formation of hafnium oxide was evidenced. Furthermore, a very homogeneous distribution of the guest oxide in the host matrix was evidenced, in agreement with SIMS data.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11577/3242594
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact