Fiber glass waste (FGW) was subjected to alkali activation in an aqueous solution with different concentrations of sodium/potassium hydroxide. The activated materials were fed into a methane–oxygen flame with a temperature of around 1600 °C. X-ray diffraction analysis confirmed the formation of several hydrated compounds, which decomposed upon flame synthesis, leading to porous glass microspheres (PGMs). Pore formation was favored by using highly concentrated activating alkali solutions. The highest homogeneity and yield of PGMs corresponded to the activation with 9 M KOH aqueous solution.
Porous Glass Microspheres from Alkali-Activated Fiber Glass Waste
Bernardo Enrico
2022
Abstract
Fiber glass waste (FGW) was subjected to alkali activation in an aqueous solution with different concentrations of sodium/potassium hydroxide. The activated materials were fed into a methane–oxygen flame with a temperature of around 1600 °C. X-ray diffraction analysis confirmed the formation of several hydrated compounds, which decomposed upon flame synthesis, leading to porous glass microspheres (PGMs). Pore formation was favored by using highly concentrated activating alkali solutions. The highest homogeneity and yield of PGMs corresponded to the activation with 9 M KOH aqueous solution.File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
materials-15-01043-v3.pdf
accesso aperto
Tipologia:
Published (publisher's version)
Licenza:
Creative commons
Dimensione
2.02 MB
Formato
Adobe PDF
|
2.02 MB | Adobe PDF | Visualizza/Apri |
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.