The fabrication of homogeneously doped germanium layers characterized by total electrical activation is currently a hot topic in many fields, such as microelectronics, photovoltaics, optics and radiation detectors. Phosphorus spin-on-doping techniquehas beenimplemented on Ge wafers, by developing a protocol for the curing process and subsequent diffusion annealing for optimal doping. Parameters such as relative humidity and curing time turned out to affect the surface morphology, the degree of reticulation reached by the dopant source and the amount of dopant available for diffusion. After spike annealing in a conventional furnace, diffusion profiles and electrical properties have been measured. Ge loss from the surface during high-temperature annealing, due to diffusion into the source film, has been observed and quantified.
Optimal process parameters for phosphorus spin-on-doping of germanium
BOLDRINI, VIRGINIA;CARTURAN, SARA MARIA;MAGGIONI, GIANLUIGI;NAPOLITANI, ENRICO;DE SALVADOR, DAVIDE
2017
Abstract
The fabrication of homogeneously doped germanium layers characterized by total electrical activation is currently a hot topic in many fields, such as microelectronics, photovoltaics, optics and radiation detectors. Phosphorus spin-on-doping techniquehas beenimplemented on Ge wafers, by developing a protocol for the curing process and subsequent diffusion annealing for optimal doping. Parameters such as relative humidity and curing time turned out to affect the surface morphology, the degree of reticulation reached by the dopant source and the amount of dopant available for diffusion. After spike annealing in a conventional furnace, diffusion profiles and electrical properties have been measured. Ge loss from the surface during high-temperature annealing, due to diffusion into the source film, has been observed and quantified.Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.