The reliability of AlGaN/GaN HEMTs adopting Fe and C co-doping, with high and low carbon doping concentration was investigated by means of different stress tests. Firstly, DC and pulsed I-V characterization at room temperature are discussed, then drain step stress tests at different gate voltages are compared, afterwards, the constant stress at different bias points are discussed. Results show that the high C HEMTs showed reduced DIBL, smaller leakage current, as well as decreased electric field, leading to an improved robustness during on-state stress testing, with respect to the reference ones. Failure modes during constant voltage stress consist in a decrease of drain current and transconductance, accelerated by temperature and electric field.
Reliability comparison of AlGaN/GaN HEMTs with different carbon doping concentration
Gao Z.;Meneghini M.;Rampazzo F.;Rzin M.;De Santi C.;Meneghesso G.;Zanoni E.
2019
Abstract
The reliability of AlGaN/GaN HEMTs adopting Fe and C co-doping, with high and low carbon doping concentration was investigated by means of different stress tests. Firstly, DC and pulsed I-V characterization at room temperature are discussed, then drain step stress tests at different gate voltages are compared, afterwards, the constant stress at different bias points are discussed. Results show that the high C HEMTs showed reduced DIBL, smaller leakage current, as well as decreased electric field, leading to an improved robustness during on-state stress testing, with respect to the reference ones. Failure modes during constant voltage stress consist in a decrease of drain current and transconductance, accelerated by temperature and electric field.Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.